Residual Stress Measurement in a Stainless Steel Clad Ferritic Plate Using the Contour Method

Naveed, Nida (2013) Residual Stress Measurement in a Stainless Steel Clad Ferritic Plate Using the Contour Method. In: ASME 2013 Pressure Vessels and Piping Conference, July 14-18, 2013, Paris, France.

[img]
Preview
PDF (Residual Stress Measurement in a Stainless Steel Clad Ferritic Plate Using the Contour Method)
PVP2013-97101.pdf - Accepted Version

Download (860kB) | Preview

Abstract

In pressure vessels stainless steel weld-overlay cladding is a widely used technique to provide a protective barrier between the corrosive environment and the ferritic low alloy base metal. While the cladding layers enhance corrosion resistance, the induced residual stresses due to the deposition of weld layers are of major concern. It is of paramount importance to understand how residual stresses interact with service loading when the vessel is pressurized. Therefore, knowledge of the initial residual stresses due to cladding is an essential input for structural integrity assessment of pressure vessels.

In the present paper the Contour Method was conducted to measure residual stresses in an austenitic steel cladded plate that was fabricated from a ferritic steel base plate with three layers of austenitic stainless steel weld metal cladding deposited on the top surface. The Contour Method was chosen for various reasons. First, it provides a full 2D variation of residual stresses over the plane of interest. Second, it is not limited by the thickness of components or microstructural variations and finally it should potentially capture the variation of residual stresses in each individual weld beads and due to the possible phase transformation in the ferritic base material. The map of longitudinal residual stresses was measured by sectioning the test component along a transverse plane at mid-length. The measured residual stresses were in good agreement with published results in the open literature

Item Type: Conference or Workshop Item (Paper)
Subjects: Engineering > Mechanical Engineering
Divisions: Faculty of Engineering and Advanced Manufacturing
Depositing User: Nida Naveed
Date Deposited: 12 Mar 2018 10:19
Last Modified: 12 Mar 2018 10:19
URI: http://sure.sunderland.ac.uk/id/eprint/8901

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year